Description:
The silk PLA filament is modified from PLA material, as easy to print as PLA. High toughness is one of PLA silk filament‘s advantages.
Selling point
Shiny and silk luster texture,
Smooth surface.
Easy to print as PLA.
High toughness.
Filament Properties Table
3D PRINTING FILAMENT
ePLA-Silk
Density(g/cm3)
1.21
Heat Distortion Temp(℃,0.45MPa)
50
Melt Flow Index(g/10min)
4.8(190℃/2.16kg)
Tensile Strength(MPa)
52
Elongation at Break(%)
14.4
Flexural Strength(MPa)
65
Flexural Modulus(MPa)
1447
IZOD Impact Strength(kJ/㎡)
5.86
Durability
4/10
Printability
9/10
Recommended printing parameters
Extruder Temperature(℃)
190 – 230℃
Recommended temperature:210℃
Bed temperature(℃)
45 – 60°C
Fan Speed
100%
Printing Speed
40 – 100mm/s
Heated Bed
Optional
Recommended Build Surfaces
Masking paper, PVP solid glue, PEI
Feature
Flexible
——
Elastic
——
Impact Resistant
——
Soft
——
Composite
——
UV Resistant
——
Water Resistant
——
Dissolvable
——
Heat Resistant
——
Chemically Resistant
——
Fatigue Resistant
——
Need drying
——
Heated Bed Required
——
Print recommend
——
Smooth surface.
Easy to print as PLA.
High toughness.
Filament Properties Table | |
---|---|
3D PRINTING FILAMENT | ePLA-Silk |
Density(g/cm3) | 1.21 |
Heat Distortion Temp(℃,0.45MPa) | 50 |
Melt Flow Index(g/10min) | 4.8(190℃/2.16kg) |
Tensile Strength(MPa) | 52 |
Elongation at Break(%) | 14.4 |
Flexural Strength(MPa) | 65 |
Flexural Modulus(MPa) | 1447 |
IZOD Impact Strength(kJ/㎡) | 5.86 |
Durability | 4/10 |
Printability | 9/10 |
Recommended printing parameters | |
Extruder Temperature(℃) | 190 – 230℃ Recommended temperature:210℃ |
Bed temperature(℃) | 45 – 60°C |
Fan Speed | 100% |
Printing Speed | 40 – 100mm/s |
Heated Bed | Optional |
Recommended Build Surfaces | Masking paper, PVP solid glue, PEI |
Feature | |
Flexible | —— |
Elastic | —— |
Impact Resistant | —— |
Soft | —— |
Composite | —— |
UV Resistant | —— |
Water Resistant | —— |
Dissolvable | —— |
Heat Resistant | —— |
Chemically Resistant | —— |
Fatigue Resistant | —— |
Need drying | —— |
Heated Bed Required | —— |
Print recommend | —— |